Cracks in Martensite Plates as Hydrogen Traps in a Bearing Steel
Change log
Authors
Abstract
It is demonstrated that a macroscopically homogeneous distribution of tiny cracks introduced into a martensitic bearing steel sample can provide powerful hydrogen traps. The phenomenon has been investigated through thermal desorption spectroscopy and hydrogen permeation measurements using both cracked and integral samples. The e↵ective hydrogen di↵usion coefficient through the cracked sample is found to be far less than in the uncracked one. Similarly, when samples are charged with hydrogen, and then subjected to thermal desorption analysis, the amount of hydrogen liberated from the cracked sample is smaller due to the trapping by the cracks. Theoretical analysis of the data shows that the traps due to cracks are so strong, that any hydrogen within the cracks can never in practice de-trap and cause harm by mechanisms that require the hydrogen to be mobile for the onset of embrittlement.
Description
Keywords
Journal Title
Conference Name
Journal ISSN
1543-1940